Elite Double 22
The Elite Double line includes a wide range of duplication silicones.
Designed to meet the lab technician’s different needs in both fixed and removable prosthesis applications. The range consists of 8 products. Elite Double has different colours, four different final hardnesses and three setting times: normal, fast and extra fast, the latter formulated specifically for automatic mixers. Elite Double retains high and constant fluidity throughout the working time, delivering a homogeneous bubble-free result.
Characteristics
• Resistance to stretching and tearing, including with thin thicknesses
• Accurate reproduction of detail
• High fluidity
• High dimensional stability over time
• High elastic recovery
Advantages
• Optimisation of working times, particularly when compared with duplication with hydrocolloids (setting time 5:00, 10:00, 20:00)
• The model can be duplicated a number of times, thanks to the dimensional stability over time and high elastic recovery
• Compatible with stones, polyurethane resins, acrylic resins and phosphate and alcohol-based investments
• High fluidity: does not require mixing in a vacuum
Zhermack recommends:
• Doublemix: automatic mixer for duplication A-Silicones
Product features
| Product | Duplication of cores, integral ceramic coating | Duplication of models, generally in gypsum and/or resin | Duplication of models, controlled expansion coating | Duplication of models, free expansion coating |
|---|---|---|---|---|
| Elite Double 8 | ● | |||
| Elite Double 16 Fast | ● | ● | ● | |
| Elite Double 16 Extra Fast | ● | ● | ● | |
| Elite Double 22 | ● | ● | ||
| Elite Double 22 Fast | ● | ● | ||
| Elite Double 22 Extra Fast | ● | ● | ||
| Elite Double 32 | ● | ● | ||
| Elite Double 32 Fast | ● | ● |
| Product | Mixing ratio | Manual mixing time* (min:s) | Mechanical mixing time with vacuum mixer* (min:s) | Working time* (min:s) | Setting time* (min:s) | Detail reproduction (μm) | Elastic recovery | Linear dimensional change (after 24 h) | Hardness (Shore A) | Load at break | Elongation at break | Tear resistance |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Elite Double 8 | 1:1 | 1:00 | 0:30 | 10:00 | 20:00 | 2 | 99.95 % | 0.05 % | 8 | 2 N/mm2 | 380 % | 2.5 N/mm2 |
| Elite Double 16 Fast | 1:1 | 1:00 | 0:30 | 5:00 | 10:00 | 2 | 99.95 % | 0.05 % | 16 | 2.5 N/mm2 | 550 % | 5 N/mm2 |
| Elite Double 16 Extra Fast | 1:1 | Automatic mixer | Automatic mixer | 1:30 | 5:00 | 2 | 99.95 % | 0.05 % | 16 | 2.5 N/mm2 | 550 % | 5 N/mm2 |
| Elite Double 22 | 1:1 | 1:00 | 0:30 | 10:00 | 20:00 | 2 | 99.95 % | 0.05 % | 22 | 2.5 N/mm2 | 450 % | 5 N/mm2 |
| Elite Double 22 Fast | 1:1 | 1:00 | 0:30 | 5:00 | 10:00 | 2 | 99.95 % | 0.05 % | 22 | 2.5 N/mm2 | 450 % | 5 N/mm2 |
| Elite Double 22 Extra Fast | 1:1 | Automatic mixer | Automatic mixer | 1:30 | 5:00 | 2 | 99.95 % | 0.05 % | 22 | 2.5 N/mm2 | 450 % | 5 N/mm2 |
| Elite Double 32 | 1:1 | 1:00 | 0:30 | 10:00 | 20:00 | 2 | 99.95 % | 0.05 % | 32 | 2.5 N/mm2 | 350 % | 5 N/mm2 |
| Elite Double 32 Fast | 1:1 | 1:00 | 0:30 | 5:00 | 10:00 | 2 | 99.95 % | 0.05 % | 32 | 2.5 N/mm2 | 350 % | 5 N/mm2 |
*The times mentioned above are intended from the start of the mixing phase at 23°C (73°F).
Packaging
| Code | Product | Packaging |
|---|---|---|
| C400821 | Elite Double 22 | 250 g (Base) + 250 g (Catalyst) |
| C400832 | Elite Double 22 | 1 kg (Base) + 1 kg (Catalyst) |
| C400840 | Elite Double 22 | 5 kg (Base) + 5 kg (Catalyst) |